聚苯胺载铂钯电极的制备及氧还原催化性能研究

李之乐 曾为民 马玉录

李之乐, 曾为民, 马玉录. 聚苯胺载铂钯电极的制备及氧还原催化性能研究[J]. 华东理工大学学报(自然科学版), 2013, (4): 466-471.
引用本文: 李之乐, 曾为民, 马玉录. 聚苯胺载铂钯电极的制备及氧还原催化性能研究[J]. 华东理工大学学报(自然科学版), 2013, (4): 466-471.
LI Zhi-le, ZENG Wei-min, MA Yu-lu. Preparation and Oxygen Reduction Catalytic Performance of Nichol Electrode with Platinum and Palladium Particles Loaded onto Polyaniline[J]. Journal of East China University of Science and Technology, 2013, (4): 466-471.
Citation: LI Zhi-le, ZENG Wei-min, MA Yu-lu. Preparation and Oxygen Reduction Catalytic Performance of Nichol Electrode with Platinum and Palladium Particles Loaded onto Polyaniline[J]. Journal of East China University of Science and Technology, 2013, (4): 466-471.

聚苯胺载铂钯电极的制备及氧还原催化性能研究

Preparation and Oxygen Reduction Catalytic Performance of Nichol Electrode with Platinum and Palladium Particles Loaded onto Polyaniline

  • 摘要: 利用恒电位法在Ni上直接电沉积Pt和Pd,制成Pt Pd/Ni电极;采用循环伏安法,在Ni片电极上电聚合导电高分子聚苯胺(PANi),然后利用恒电位法在聚苯胺薄膜上制备了聚苯胺载Pt Pd复合电极(Pt Pd PANi/Ni)。采用线性伏安扫描法、交流阻抗法、扫描电镜、能谱方法对电极催化剂进行测试表征,实验表明:将Pt Pd沉积在聚苯胺上,增加了Pt Pd颗粒的分散度,Pt Pd的利用率得以提高,Pt Pd晶体颗粒大小为1~5 μm。在相同的Pt Pd载量下,Pt Pd PANi/Ni电极比Pt Pd/Ni电极对氧还原的催化性能更好。在Ni片上沉积聚苯胺5个周期后再沉积Pt Pd 600 s时的Pt Pd PANi/Ni电极对氧还原的催化效果最好。

     