    丙烯腈/丙烯酰胺/苯乙烯三元共聚超滤膜材料的制备和表征

    Synthesis and Characterrization of the Ultrafiltration Membrane Materials of Poly (acrylonitrile-acrylamide-styrene)

      摘要
    • 摘要: 以偶氮二异丁腈为引发剂,采用溶液聚合法制备了丙烯腈、丙烯酰胺、苯乙烯三元共聚物,并用红外光谱(IR)、示差扫描量热(DSC)、热重分析(TG)等手段对共聚物进行了结构和性能表征。结果表明:苯乙烯的加入使得参加环化反应的氰基和酰胺基的数目减少,保留了更多作为功能基团的酰胺基。用相转化法制备得到超滤平板膜,膜的渗透通量为2.63 mL/(cm2.h),对聚乙二醇20000(PEG 20000)的截留率为96.95%。

       