    渗透蒸发膜的研制:聚丙烯酸与聚乙烯醇等共混及其缩醛化

    Preparation of Polyvinyl Alcohol/Polyacrylic Acid Pervaporation Membrane Modified by Blending and Acetal Reaction

    • 摘要: 以乙醇水溶液为分离对象,研究了聚丙烯酸(PAA)与聚酰胺羧或聚乙烯醇(PVA)共混膜的渗透蒸发分离性能,以及均相,非均相缩醛反应对PVA膜分离因素α和渗透通量J的影响。实验发现,戊二醛交联PVA膜的α提高 到49.5(乙醇含水C1=10%,温度为55℃);增加非均相缩甲醛反应时间,PVA/PAA共混膜的α先下降而后趋于不变,同时J存在一最大值。

       

    /