    蔡兰坤, 张东曙, 祝鸿范, 周浩. 防止银器文物变色的唑系复合缓蚀剂——I.缓蚀剂成膜处理工艺与防变色性能的评定[J]. 华东理工大学学报（自然科学版）, 2002, (3).
    引用本文: 蔡兰坤, 张东曙, 祝鸿范, 周浩. 防止银器文物变色的唑系复合缓蚀剂——I.缓蚀剂成膜处理工艺与防变色性能的评定[J]. 华东理工大学学报（自然科学版）, 2002, (3).
    shu
    Azoles as Composite Corrosion Inhibitor for Anti tarnishing of Silver Antiques I. Process of the Inhibition Film Formation and Assessment of Its Anti tarnishing Abilities[J]. Journal of East China University of Science and Technology, 2002, (3).
    Citation: Azoles as Composite Corrosion Inhibitor for Anti tarnishing of Silver Antiques I. Process of the Inhibition Film Formation and Assessment of Its Anti tarnishing Abilities[J]. Journal of East China University of Science and Technology, 2002, (3).
    shu

    防止银器文物变色的唑系复合缓蚀剂——I.缓蚀剂成膜处理工艺与防变色性能的评定

    Azoles as Composite Corrosion Inhibitor for Anti tarnishing of Silver Antiques I. Process of the Inhibition Film Formation and Assessment of Its Anti tarnishing Abilities

      摘要
    • 摘要: :通过按正交法设计的紫外光照曝露等加速大气腐蚀实验 ,研究了用于防止银变色的唑系复合缓蚀剂成膜处理的工艺 ,并评定其对模拟文物银试片的防变色性能。采用极化曲线和交流阻抗Nyquist图 ,讨论了防变色作用的电化学机理。实验结果表明 ,缓蚀剂 PMTA、MBI和 MBO具有较好的协同作用 ,银试片在 5 0°C、p H 3.0、组分 MBO∶ PMTA∶ MBI为 1∶ 1 .7∶ 3(摩尔比 )、复合缓蚀剂浓度为 0 .0 1 89mol/L的溶液中 4h成膜处理后 ,经 48h硫华气氛和 36h紫外光曝露腐蚀实验 ,无色斑出现 ,表明缓蚀膜明显地提高了银试片的抗变色能力

       